Tribocorrosive behaviour of low temperature plasma-nitrided PH stainless steel sliding against alumina under linear reciprocation with and without transverse oscillations
In this work, precipitation hardening (PH) stainless steel was plasma nitrided at low temperatures 400oC and 425oC for 15 h. The wear and corrosion-wear behaviour of the untreated and nitrided specimens were investigated under both dry sliding and wet sliding (in 3% NaCl solution) conditions, using both one-dimensional (1D) and two-dimensional (2D) reciprocating motions. The 2D motion was realised by reciprocating the sample stage as the primary motion and at the same time reciprocating the ball (pin) holder at a high frequency and small amplitude as the secondary motion. The results show that 2D sliding has significant effects on the wear behaviour of the test specimens. Under dry condition, 2D sliding leads to a significant increase in wear volume by 70% to 230%. Nitriding is very effective in increasing dry sliding wear resistance of the steel under both 1D and 2D conditions, with 400oC nitriding being the most effective. Under corrosion-wear (tribocorrosion) condition in 3% NaCl solution, 2D sliding leads to a more significant drop in open circuit potential (OCP) and a more significant increase in anodic current than 1D sliding. While under 1D sliding condition, nitriding is effective in reducing material removal by tribocorrosion, under 2D sliding condition, the effectiveness of nitriding is dependent on nitriding temperature. Nitriding at 425oC results in accelerated material removal during 2D sliding in the corrosive solution. The mechanisms of material removal are discussed in terms of the structures of the nitride layers and their electrochemical response to the corrosive solution.
Citation : Sun, Y. (2016) Tribocorrosive behaviour of low temperature plasma-nitrided PH stainless steel sliding against alumina under linear reciprocation with and without transverse oscillations. Wear, 362-363, pp.105-113
Research Group : Emerging Technologies Research Centre
Research Institute : Institute of Engineering Sciences (IES)
Peer Reviewed : Yes